Thermal Conductivity Of High Alumina Bricks

Thermal conductivity of high alumina bricks are higher than fire clay bricks. The reason is that there are few glass phases with low thermal conductivity in high alumina bricks, while the mullite and corundum crystal with better thermal conductivity increases, which improves the thermal conductivity of products. This article is from RS Kiln Company to tell you about thermal conductivity of high alumina bricks.

High Alumina Bricks With Good Thermal Conductivity
High Alumina Bricks.

Get Free Quote

Your Name (required)

Your Email (required)

Your Phone

Your Message (required)

The thermal conductivity of high alumina bricks is different from that of clay bricks and silica bricks. The thermal conductivity of high alumina bricks decreases with the increase of temperature, and the higher the Al2O3 content in the high alumina bricks, the more the mullite and the corundum crystal content, then the thermal conductivity decreases with the increase of temperature. But at 1000 degrees Celsius, the relationship between the Al2O3 content and decrease in the softening temperature of the load is not obvious. The thermal conductivity of fire clay brick and silicon brick increases with the increase of temperature in a linear relationship, and does not change near 1000 degrees Celsius.

Qualified High Alumina Bricks For Sale In RS
Qualified High Alumina Bricks.

Get Free Quote

Your Name (required)

Your Email (required)

Your Phone

Your Message (required)

At room temperature, the thermal conductivity of high alumina bricks is 2-3 times higher than that of fire clay bricks, but above 1000 degrees Celsius, the thermal conductivity is basically similar. The main disadvantage of fire clay bricks is that the softening point of load is low. The reason is that the fire clay brick will produce a large amount of liquid phases at lower temperature, making the use temperature low. The kind of refractory bricks with low Al2O3 is similar to fire clay brick. But with the increase of Al2O3 content, the softening point of the load increases gradually. The thermal shock resistance of high alumina bricks is basically the same as that of fire clay bricks except for those with Al2O3 content.

High Alumina Bricks By RS With Good Thermal Conductivity
High Alumina Bricks By RS.

Get Free Quote

Your Name (required)

Your Email (required)

Your Phone

Your Message (required)

These characteristics of high alumina bricks make them suitable for high temperature parts of glass melting furnace. The kind with low porosity can be used in high temperature parts of regenerator, such as the top and upper wall of regenerator. This kind of high alumina bricks can also be used in the contact area between feed machine and glass liquid. The high alumina bricks with proper porosity have good thermal shock resistance and can be applied to the accessories of the feeder and the top of the material path. Want to know more about thermal conductivity of high alumina bricks? Come and find RS Kiln Refractory Company! Want to buy qualified high alumian bricks? Email RS For Cheap High Alumina Bricks!

Cheap Refractories Materials For Sale In RS Factory. Email Us For Price Now!